Hello, I’d like to enter my material’s sorption isotherm in the database. However, it presents a high hysteretic behavior. Since Wufi does not consider the desorption curve, would it be better to enter only the adsorption curve, or should I make an average curve between adsorption and desorption cur...

Hello Thomas ! Thank you a lot ! Indeed, I am also performing the water absorption experiment as you guessed ! Your information will be very useful to compare my experimental data to WUFI results. In this case, I suppose I have to set all the surfaces to adiabatic (except the one in contact with wat...

Hi Thomas,

thank you for your answer.

I am trying to simulate the same case as Chin Peng. Therefore, I have a question:

-Can I use the tab "sources, sinks" to create the rising damp in the lower part of the wall instead of adding a new climate file?

Thank you!

Lorena